ΜΕΛΕΤΗ ΚΑΙ ΠΑΡΑΣΚΕΥΗ ΚΥΨΕΛΩΤΟΥ ΚΟΝΙΟΔΕΜΑΤΟΣ ΥΔΡΟΘΕΡΜΙΚΗΣ ΚΑΤΕΡΓΑΣΙΑΣ ΜΕ ΜΕΙΩΜΕΝΕΣ ΣΥΣΤΟΛΕΣ ΞΗΡΑΝΣΗΣ

THIS THESIS PRESENTS THE IN-DEPTH STUDY AND THE EFFECTIVE CONTROL OF THE PROBLEM ARISING FROM DRYING SHRINKAGE HIGH VALUES DETECTED AT AUTOCLAVED CELLULAR CONCRETE (A.C.C.). FROM THE PROCESSING AND EVALUATION OF THE EXPERIMENTAL MEASUREMENTS THE FOLLOWING CONCLUSIONS HAVE BEEN REACHED: A. THERE IS A DIRECT CORRELATION BETWEEN THE DRYING SHRINKAGE VALUES AND THE PERCENTAGE OF 11A-TOBERMORITE AND AL-TOBERMORITE CONTENT IN A.C. C. B. ON THE BASIS OF MINERALOGICAL COMPOSITION AND MICROPORE SIZE DISTRIBUTION OF A.C.C., THE DRYING SHRINKAGE VALUES SHOULD BE WITHIN THE REALM OF PREDICTABILITY. A PRACTICAL APPLICATION OF THE STUDY HAS BEEN THE SUCCESSFUL UTILIZATION OF PTOLEMAIS FLY ASH IN THE DOMESTIC A.C.C. PRODUCTION.

Grantor dc:publisher

Εθνικό Μετσόβιο Πολυτεχνείο (ΕΜΠ)

Year dc:date

1990

Author dc:creator

• Γεωργιάδης, Ανδρέας

• AERATED CONCRETE
• Cellular concrete
• Drying shrinkage
• FOAM CONCRETE
• HYDROTHERMALLY TREATED CELLULAR CONCRETE
• PORE STRUCTURE OF CELLULAR CONCRETE
• ΑΕΡΙΟΜΠΕΤΟΝ
• ΑΦΡΟΜΠΕΤΟΝ
• ΚΥΨΕΛΩΤΟ ΚΟΝΙΟΔΕΜΑ ΥΔΡΟΘΕΡΜΙΚΗΣ ΚΑΤΕΡΓΑΣΙΑΣ
• Κυψελωτό μπετόν
• ΠΟΡΩΔΗΣ ΔΟΜΗ ΤΟΥ ΚΥΨΕΛΩΤΟΥ ΜΠΕΤΟΝ
• ΣΥΣΤΟΛΕΣ ΞΗΡΑΝΣΗΣ
• Engineering and Technology
• Chemical Engineering
• Επιστήμες Μηχανικού και Τεχνολογία
• Επιστήμη Χημικού Μηχανικού

Language dc:language

gre

Identifier

10.12681/eadd/1421

OAI identifier oai:identifier

oai:10442/1421