The Degradation of Resin Materials Bonded to Dentine in the Root Canal by the Activation of Matrix Metalloproteinases
type: CreativeWork
description: Despite all the improvements resin based adhesive dental restorative materials have gone through in the last two decades, leakage in the resin-dentine interface is still a major limitation of resin based dental restorative materials. Dentine matrix metalloproteinases have been associated with this leakage through their involvement in the proteolytic degradation of the resin-dentine hybrid layer. The inhibitory effect of chlorhexidine on this enzymatic activity is well established. Bioactive glass materials can also reduce the resin-dentine interface leakage through biomimetic remineralisation of the dentine. In this study the commercially available self-adhesive self-cure resin cement RelyXTM Unicem AplicapTM was modified by incorporating chlorhexidine and Bioglass 45S5 into the cement composition. The evaluation of the physical properties of the modified cement has shown that the original physical properties of the RelyXTM Unicem AplicapTM cement were not adversely affected by these modifications. One hundred and fifty dentine specimens were obtained from human permanent single-rooted teeth and restored with the test cements. The test cements’ push-out bond strength was measured and statistically analysed after ageing the specimens in artificial saliva for one week and after nine months. The matrix metalloproteinases activity was also quantified after each storage period. The study results showed that incorporating chlorhexidine and Bioglass 45S5 jointly or separately into the composition of RelyXTM Unicem AplicapTM did reduce MMP-2 activity after the short- and long-term storage. It was also shown by the results of this work that incorporating chlorhexidine and Bioglass 45S5 jointly, and chlorhexidine separately into the composition of the cement also reduced MMP-9 activity after short and long-term storage. Statistical analyses of the test results has shown that incorporating chlorhexidine and Bioglass 45S5 into the RelyXTM Unicem AplicapTM cement composition sig…
abstract: Despite all the improvements resin based adhesive dental restorative materials have gone through in the last two decades, leakage in the resin-dentine interface is still a major limitation of resin based dental restorative materials. Dentine matrix metalloproteinases have been associated with this leakage through their involvement in the proteolytic degradation of the resin-dentine hybrid layer. The inhibitory effect of chlorhexidine on this enzymatic activity is well established. Bioactive glass materials can also reduce the resin-dentine interface leakage through biomimetic remineralisation of the dentine. In this study the commercially available self-adhesive self-cure resin cement RelyXTM Unicem AplicapTM was modified by incorporating chlorhexidine and Bioglass 45S5 into the cement composition. The evaluation of the physical properties of the modified cement has shown that the original physical properties of the RelyXTM Unicem AplicapTM cement were not adversely affected by these modifications. One hundred and fifty dentine specimens were obtained from human permanent single-rooted teeth and restored with the test cements. The test cements’ push-out bond strength was measured and statistically analysed after ageing the specimens in artificial saliva for one week and after nine months. The matrix metalloproteinases activity was also quantified after each storage period. The study results showed that incorporating chlorhexidine and Bioglass 45S5 jointly or separately into the composition of RelyXTM Unicem AplicapTM did reduce MMP-2 activity after the short- and long-term storage. It was also shown by the results of this work that incorporating chlorhexidine and Bioglass 45S5 jointly, and chlorhexidine separately into the composition of the cement also reduced MMP-9 activity after short and long-term storage. Statistical analyses of the test results has shown that incorporating chlorhexidine and Bioglass 45S5 into the RelyXTM Unicem AplicapTM cement composition sig…
author: Alharbi, Ali A.
language: eng
date published: 2017
date modified: 2026-07-24T02:08:26Z
provider: University of Dundee
publisher: Networked Digital Library of Theses and Dissertations
type: WebPage
source organization: University of Dundee