The effects of sequence of impregnation (Pd on cerium oxides -alumina and cerium oxides on Pd-alumina) and calcination temperature (500 ℃ and 850 ℃) on the catalytic oxidation of methane under lean conditions were investigated. The catalysts were prepared by a combination of impregnation, slurry and vortexing methods. The catalysts had 4.7 wt.% Pd and 10.7 wt.% Ce based on inductively coupled plasma optical emission spectrometry (ICP-OES) analysis. The catalysts were characterized by pulse chemisorption, temperature programmed reduction (TPD), scanning transmission electron microscopy (STEM), and X-ray photoelectron spectroscopy (XPS). The activity of the catalysts for methane combustion was measured in a fixed-bed flow reactor by flowing a gas mix (0.98 vol % methane, 4.01 vol % and balance nitrogen) through a catalytic bed. The temperature of the catalytic bed was controlled by a temperature -controlled tube furnace. The % methane in the effluent gas mix was measured by a gas chromatograph fitted with a flame ionization detector and a ‘Carbon Plot’ column. Palladium was present as PdO and PdOx x>2+ and cerium as CeOx (+3 and +4 oxidation states) as per XPS analysis. The activity of the Pd/cerium oxides-alumina500C catalyst was higher than the cerium oxides/Pd-alumina500C catalyst at 250-500 ℃. Similar trends in the activity were seen for the two catalysts calcined at 850 ℃. Higher dispersion and lower particle size, and the presence of small Pd particles on alumina accounted for the higher catalytic activities of the Pd/cerium oxides-alumina500C and 850C catalysts. The lower activities of cerium oxides/Pd-alumina500C and 850C were primarily due to the embedment of Pd onto ceria due to strong PdO-CeOx interactions. This research implies that the sequence of impregnation and calcination temperature could alter catalytic properties and activity for methane combustion through PdO/PdOx -support interactions.
","abstract_html":"<p>The effects of sequence of impregnation (Pd on cerium oxides -alumina and cerium oxides on Pd-alumina) and calcination temperature (500 ℃ and 850 ℃) on the catalytic oxidation of methane under lean conditions were investigated. The catalysts were prepared by a combination of impregnation, slurry and vortexing methods. The catalysts had 4.7 wt.% Pd and 10.7 wt.% Ce based on inductively coupled plasma optical emission spectrometry (ICP-OES) analysis. The catalysts were characterized by pulse chemisorption, temperature programmed reduction (TPD), scanning transmission electron microscopy (STEM), and X-ray photoelectron spectroscopy (XPS). The activity of the catalysts for methane combustion was measured in a fixed-bed flow reactor by flowing a gas mix (0.98 vol % methane, 4.01 vol % and balance nitrogen) through a catalytic bed. The temperature of the catalytic bed was controlled by a temperature -controlled tube furnace. The % methane in the effluent gas mix was measured by a gas chromatograph fitted with a flame ionization detector and a ‘Carbon Plot’ column. Palladium was present as PdO and PdOx x>2+ and cerium as CeOx (+3 and +4 oxidation states) as per XPS analysis. The activity of the Pd/cerium oxides-alumina500C catalyst was higher than the cerium oxides/Pd-alumina500C catalyst at 250-500 ℃. Similar trends in the activity were seen for the two catalysts calcined at 850 ℃. Higher dispersion and lower particle size, and the presence of small Pd particles on alumina accounted for the higher catalytic activities of the Pd/cerium oxides-alumina500C and 850C catalysts. The lower activities of cerium oxides/Pd-alumina500C and 850C were primarily due to the embedment of Pd onto ceria due to strong PdO-CeOx interactions. This research implies that the sequence of impregnation and calcination temperature could alter catalytic properties and activity for methane combustion through PdO/PdOx -support interactions.</p>","abstract_has_math":false,"creators":["Park, Jihyeon"],"institution":null,"degree_name":"Chemistry","degree_level":"Thesis","degree_discipline":"Chemistry","degree_department":null,"school":null,"contributors":["Dr. Anil C. Banerjee","Dr. Zewdu Gebeyehu","Dr. Daniel Wade Holley"],"advisors":[],"committee_chairs":[],"committee_members":[],"year":2022,"date_issued":"2022-04-26T07:00:00Z","date_published":"2022-04-26T07:00:00Z","updated_at":"2026-07-24T01:45:08Z","subjects":["Impregnation Sequence","Catalyst Preparation Methods","Methane Combustion","Characterization","Metal-Support Interactions","Chemistry","Inorganic Chemistry"],"languages":["English"],"rights":[],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"https://csuepress.columbusstate.edu/theses_dissertations/468","outbound_label":"Repository record","outbound_source":"dc:identifier"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor","label":"Contributor","values":["Dr. Anil C. Banerjee","Dr. Zewdu Gebeyehu","Dr. Daniel Wade Holley"]},{"key":"dc:creator","label":"Author","values":["Park, Jihyeon"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.available","label":"Dc Date Available","values":["2022-04-28T07:00:00Z"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Chemistry"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Thesis"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Chemistry"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Impregnation Sequence","Catalyst Preparation Methods","Methane Combustion","Characterization","Metal-Support Interactions","Chemistry","Inorganic Chemistry"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["English"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["https://csuepress.columbusstate.edu/theses_dissertations/468"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["The effects of sequence of impregnation (Pd on cerium oxides -alumina and cerium oxides on Pd-alumina) and calcination temperature (500 ℃ and 850 ℃) on the catalytic oxidation of methane under lean conditions were investigated. The catalysts were prepared by a combination of impregnation, slurry and vortexing methods. The catalysts had 4.7 wt.% Pd and 10.7 wt.% Ce based on inductively coupled plasma optical emission spectrometry (ICP-OES) analysis. The catalysts were characterized by pulse chemisorption, temperature programmed reduction (TPD), scanning transmission electron microscopy (STEM), and X-ray photoelectron spectroscopy (XPS). The activity of the catalysts for methane combustion was measured in a fixed-bed flow reactor by flowing a gas mix (0.98 vol % methane, 4.01 vol % and balance nitrogen) through a catalytic bed. The temperature of the catalytic bed was controlled by a temperature -controlled tube furnace. The % methane in the effluent gas mix was measured by a gas chromatograph fitted with a flame ionization detector and a ‘Carbon Plot’ column. Palladium was present as PdO and PdOx x>2+ and cerium as CeOx (+3 and +4 oxidation states) as per XPS analysis. The activity of the Pd/cerium oxides-alumina500C catalyst was higher than the cerium oxides/Pd-alumina500C catalyst at 250-500 ℃. Similar trends in the activity were seen for the two catalysts calcined at 850 ℃. Higher dispersion and lower particle size, and the presence of small Pd particles on alumina accounted for the higher catalytic activities of the Pd/cerium oxides-alumina500C and 850C catalysts. The lower activities of cerium oxides/Pd-alumina500C and 850C were primarily due to the embedment of Pd onto ceria due to strong PdO-CeOx interactions. This research implies that the sequence of impregnation and calcination temperature could alter catalytic properties and activity for methane combustion through PdO/PdOx -support interactions.
"]},{"key":"dc:title","label":"Title","values":["Synthesis, Characterization and Activity of Palladium Catalysts on the Dual Support of Cerium and Aluminum Oxides"]}]}],"canonical_facts":{"dc:contributor":["Dr. Anil C. Banerjee","Dr. Zewdu Gebeyehu","Dr. Daniel Wade Holley"],"dc:creator":["Park, Jihyeon"],"dc:date.available":["2022-04-28T07:00:00Z"],"dc:description.abstract":["The effects of sequence of impregnation (Pd on cerium oxides -alumina and cerium oxides on Pd-alumina) and calcination temperature (500 ℃ and 850 ℃) on the catalytic oxidation of methane under lean conditions were investigated. The catalysts were prepared by a combination of impregnation, slurry and vortexing methods. The catalysts had 4.7 wt.% Pd and 10.7 wt.% Ce based on inductively coupled plasma optical emission spectrometry (ICP-OES) analysis. The catalysts were characterized by pulse chemisorption, temperature programmed reduction (TPD), scanning transmission electron microscopy (STEM), and X-ray photoelectron spectroscopy (XPS). The activity of the catalysts for methane combustion was measured in a fixed-bed flow reactor by flowing a gas mix (0.98 vol % methane, 4.01 vol % and balance nitrogen) through a catalytic bed. The temperature of the catalytic bed was controlled by a temperature -controlled tube furnace. The % methane in the effluent gas mix was measured by a gas chromatograph fitted with a flame ionization detector and a ‘Carbon Plot’ column. Palladium was present as PdO and PdOx x>2+ and cerium as CeOx (+3 and +4 oxidation states) as per XPS analysis. The activity of the Pd/cerium oxides-alumina500C catalyst was higher than the cerium oxides/Pd-alumina500C catalyst at 250-500 ℃. Similar trends in the activity were seen for the two catalysts calcined at 850 ℃. Higher dispersion and lower particle size, and the presence of small Pd particles on alumina accounted for the higher catalytic activities of the Pd/cerium oxides-alumina500C and 850C catalysts. The lower activities of cerium oxides/Pd-alumina500C and 850C were primarily due to the embedment of Pd onto ceria due to strong PdO-CeOx interactions. This research implies that the sequence of impregnation and calcination temperature could alter catalytic properties and activity for methane combustion through PdO/PdOx -support interactions.
"],"dc:identifier":["https://csuepress.columbusstate.edu/theses_dissertations/468"],"dc:language":["English"],"dc:subject":["Impregnation Sequence","Catalyst Preparation Methods","Methane Combustion","Characterization","Metal-Support Interactions","Chemistry","Inorganic Chemistry"],"dc:title":["Synthesis, Characterization and Activity of Palladium Catalysts on the Dual Support of Cerium and Aluminum Oxides"],"thesis:degree_discipline":["Chemistry"],"thesis:degree_level":["Thesis"],"thesis:degree_name":["Chemistry"]},"updated_at":"2026-07-24T01:45:08Z"}