{"id":{"repo_id":"colo-mines","oai_identifier":"oai:repository.mines.edu:11124/20149"},"canonical_url":"https://search.dev.ndltd.org/etd/colo-mines/oai:repository.mines.edu:11124/20149","repository":{"repo_id":"colo-mines","name":"Colorado School of Mines","base_url":"https://repository.mines.edu/server/oai/request"},"display":{"title":"Investigation of carburization extent from the inner diameter (ID) of ethylene furnace tubes using non-destructive examination (NDE) applied on the outer diameter (OD)","abstract":"This research project is to investigate the possibility of measuring the depth and location of carburization and metal dusting on the inside of ethylene pyrolysis tubes using nondestructive tools applied to the outer surface. A carburization test was conducted in a specially designed and manufactured HK-40 alloy tube. Ethylene pyrolysis is considered the most important process in the petrochemical industry for producing petrochemical products. Some furnace tubes used for ethylene pyrolysis often suffer severe high-temperature corrosion since the tube surfaces are heated up to about 1,100 0C in contact with steam-hydrocarbon gas mixtures. Simultaneous carbon deposition on the tube surfaces (i.e. coking) can deteriorate the mechanical properties of the tube materials and may result in a failure of the furnace tubes in the form of carburization or metal dusting. This investigation consists of four separate experimental practices to detect and assess the carburization and metal dusting damage. It involves a) impulse testing to study changes in natural elastic wave frequencies, b) metallographic evaluation, c) resonant ultrasound spectroscopy (RUS), and d) computational modeling to simulate guided wave and ultrasonic phased array technique. The collaboration of the results of these experiments demonstrated the possibility that ultrasonic phased array can offer an efficient and economical practice to determine the remaining services life of the ethylene furnace tubes. The elastic responses (frequency shift and mode shape changes) of the HK-40 alloy tube was studied due to changes in material properties that result from carburization and metal dusting, a severe form of carburization. Natural frequency analysis was conducted as measured at different locations of the HK-40 alloy tube before and after the carburization test. A shift in natural frequencies was observed and is understood to be due to a reduction in shear wave speed in the carburized samples. This shift seems to correlate to the extent of carburization and forms the basis for a new nondestructive evaluation method. Extensive metallographic examination of transverse and longitudinal cross section samples cut out of the HK-40 alloy tube after carburization using optical macrograph, scanning electron microscopy and energy dispersive X-ray were used to quantify the carburization extent as compared to the corresponding shift in natural frequencies. Computational modeling using a finite element analysis program (COMSOL) was used to simulate different scenarios of alternating the material properties, depth and shape of carburization and metal dusting. The simulations revealed strong reflections from relatively high defect depth to tube thickness ratio based on exciting a guided wave. Relatively small defects were very weak in terms of wave reflection amplitude. Hence, phased array technique was utilized in the simulation to enhance the use of guided wave by amplifying the low peak amplitude of the reflected wave from defects. The research reported provides a new approach to advanced nondestructive testing to evaluate the remaining life of ethylene furnace tubes and other application tubes suffering carburization and metal dusting.","abstract_html":"This research project is to investigate the possibility of measuring the depth and location of carburization and metal dusting on the inside of ethylene pyrolysis tubes using nondestructive tools applied to the outer surface. A carburization test was conducted in a specially designed and manufactured HK-40 alloy tube. Ethylene pyrolysis is considered the most important process in the petrochemical industry for producing petrochemical products. Some furnace tubes used for ethylene pyrolysis often suffer severe high-temperature corrosion since the tube surfaces are heated up to about 1,100 0C in contact with steam-hydrocarbon gas mixtures. Simultaneous carbon deposition on the tube surfaces (i.e. coking) can deteriorate the mechanical properties of the tube materials and may result in a failure of the furnace tubes in the form of carburization or metal dusting. This investigation consists of four separate experimental practices to detect and assess the carburization and metal dusting damage. It involves a) impulse testing to study changes in natural elastic wave frequencies, b) metallographic evaluation, c) resonant ultrasound spectroscopy (RUS), and d) computational modeling to simulate guided wave and ultrasonic phased array technique. The collaboration of the results of these experiments demonstrated the possibility that ultrasonic phased array can offer an efficient and economical practice to determine the remaining services life of the ethylene furnace tubes. The elastic responses (frequency shift and mode shape changes) of the HK-40 alloy tube was studied due to changes in material properties that result from carburization and metal dusting, a severe form of carburization. Natural frequency analysis was conducted as measured at different locations of the HK-40 alloy tube before and after the carburization test. A shift in natural frequencies was observed and is understood to be due to a reduction in shear wave speed in the carburized samples. This shift seems to correlate to the extent of carburization and forms the basis for a new nondestructive evaluation method. Extensive metallographic examination of transverse and longitudinal cross section samples cut out of the HK-40 alloy tube after carburization using optical macrograph, scanning electron microscopy and energy dispersive X-ray were used to quantify the carburization extent as compared to the corresponding shift in natural frequencies. Computational modeling using a finite element analysis program (COMSOL) was used to simulate different scenarios of alternating the material properties, depth and shape of carburization and metal dusting. The simulations revealed strong reflections from relatively high defect depth to tube thickness ratio based on exciting a guided wave. Relatively small defects were very weak in terms of wave reflection amplitude. Hence, phased array technique was utilized in the simulation to enhance the use of guided wave by amplifying the low peak amplitude of the reflected wave from defects. The research reported provides a new approach to advanced nondestructive testing to evaluate the remaining life of ethylene furnace tubes and other application tubes suffering carburization and metal dusting.","abstract_has_math":false,"creators":["Alharbi, Wael Abdulelah"],"institution":"Colorado School of Mines. Arthur Lakes Library","degree_name":"Doctor of Philosophy (Ph.D.)","degree_level":"Doctoral","degree_discipline":"Metallurgical and Materials Engineering","degree_department":null,"school":null,"contributors":[],"advisors":["Olson, D. L. (David LeRoy)","Mishra, Brajendra"],"committee_chairs":[],"committee_members":["Liu, Stephen","Meegan, Douglas","Lasseigne, Angelique","Mataya, Martin"],"year":2015,"date_issued":"2015","date_published":"2015","updated_at":"2026-07-24T01:43:42Z","subjects":["metal dusting","carburization","non-destructive examination"],"languages":["eng","English"],"rights":["Copyright of the original work is retained by the author."],"rights_urls":[],"identifier_entries":[{"key":"dc:identifier","label":"Identifier","values":["T 7847"],"render_values":[{"text":"T 7847","href":null,"code":true}]}]},"links":{"outbound_url":"https://hdl.handle.net/11124/20149","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.advisor","label":"Advisor","values":["Olson, D. L. (David LeRoy)","Mishra, Brajendra"]},{"key":"dc:contributor.committeemember","label":"Committee Member","values":["Liu, Stephen","Meegan, Douglas","Lasseigne, Angelique","Mataya, Martin"]},{"key":"dc:creator","label":"Author","values":["Alharbi, Wael Abdulelah"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2015-09-10T15:54:55Z","2022-02-03T12:50:52Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2016-08-28T04:18:44Z","2022-02-03T12:50:52Z"]},{"key":"dc:date.issued","label":"Date","values":["2015"]},{"key":"dc:publisher","label":"Institution","values":["Colorado School of Mines. Arthur Lakes Library"]},{"key":"dc:type","label":"Dc Type","values":["Text"]},{"key":"thesis:degree_discipline","label":"Discipline","values":["Metallurgical and Materials Engineering"]},{"key":"thesis:degree_level","label":"Degree Level","values":["Doctoral"]},{"key":"thesis:degree_name","label":"Degree Name","values":["Doctor of Philosophy (Ph.D.)"]},{"key":"thesis:institution_name","label":"Thesis Institution Name","values":["Colorado School of Mines"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["metal dusting","carburization","non-destructive examination"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["English"]},{"key":"dc:language.iso","label":"Language (ISO)","values":["eng"]},{"key":"dc:rights","label":"Dc Rights","values":["Copyright of the original work is retained by the author."]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier","label":"Identifier","values":["T 7847"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["https://hdl.handle.net/11124/20149"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description","label":"Description","values":["2015 Fall.","Includes illustrations (some color).","Includes bibliographical references."]},{"key":"dc:description.abstract","label":"Abstract","values":["This research project is to investigate the possibility of measuring the depth and location of carburization and metal dusting on the inside of ethylene pyrolysis tubes using nondestructive tools applied to the outer surface. A carburization test was conducted in a specially designed and manufactured HK-40 alloy tube. Ethylene pyrolysis is considered the most important process in the petrochemical industry for producing petrochemical products. Some furnace tubes used for ethylene pyrolysis often suffer severe high-temperature corrosion since the tube surfaces are heated up to about 1,100 0C in contact with steam-hydrocarbon gas mixtures. Simultaneous carbon deposition on the tube surfaces (i.e. coking) can deteriorate the mechanical properties of the tube materials and may result in a failure of the furnace tubes in the form of carburization or metal dusting. This investigation consists of four separate experimental practices to detect and assess the carburization and metal dusting damage. It involves a) impulse testing to study changes in natural elastic wave frequencies, b) metallographic evaluation, c) resonant ultrasound spectroscopy (RUS), and d) computational modeling to simulate guided wave and ultrasonic phased array technique. The collaboration of the results of these experiments demonstrated the possibility that ultrasonic phased array can offer an efficient and economical practice to determine the remaining services life of the ethylene furnace tubes. The elastic responses (frequency shift and mode shape changes) of the HK-40 alloy tube was studied due to changes in material properties that result from carburization and metal dusting, a severe form of carburization. Natural frequency analysis was conducted as measured at different locations of the HK-40 alloy tube before and after the carburization test. A shift in natural frequencies was observed and is understood to be due to a reduction in shear wave speed in the carburized samples. This shift seems to correlate to the extent of carburization and forms the basis for a new nondestructive evaluation method. Extensive metallographic examination of transverse and longitudinal cross section samples cut out of the HK-40 alloy tube after carburization using optical macrograph, scanning electron microscopy and energy dispersive X-ray were used to quantify the carburization extent as compared to the corresponding shift in natural frequencies. Computational modeling using a finite element analysis program (COMSOL) was used to simulate different scenarios of alternating the material properties, depth and shape of carburization and metal dusting. The simulations revealed strong reflections from relatively high defect depth to tube thickness ratio based on exciting a guided wave. Relatively small defects were very weak in terms of wave reflection amplitude. Hence, phased array technique was utilized in the simulation to enhance the use of guided wave by amplifying the low peak amplitude of the reflected wave from defects. The research reported provides a new approach to advanced nondestructive testing to evaluate the remaining life of ethylene furnace tubes and other application tubes suffering carburization and metal dusting."]},{"key":"dc:format.medium","label":"Dc Format Medium","values":["born digital","doctoral dissertations"]},{"key":"dc:title","label":"Title","values":["Investigation of carburization extent from the inner diameter (ID) of ethylene furnace tubes using non-destructive examination (NDE) applied on the outer diameter (OD)"]}]}],"canonical_facts":{"dc:contributor.advisor":["Olson, D. L. (David LeRoy)","Mishra, Brajendra"],"dc:contributor.committeemember":["Liu, Stephen","Meegan, Douglas","Lasseigne, Angelique","Mataya, Martin"],"dc:creator":["Alharbi, Wael Abdulelah"],"dc:date.accessioned":["2015-09-10T15:54:55Z","2022-02-03T12:50:52Z"],"dc:date.available":["2016-08-28T04:18:44Z","2022-02-03T12:50:52Z"],"dc:date.issued":["2015"],"dc:description":["2015 Fall.","Includes illustrations (some color).","Includes bibliographical references."],"dc:description.abstract":["This research project is to investigate the possibility of measuring the depth and location of carburization and metal dusting on the inside of ethylene pyrolysis tubes using nondestructive tools applied to the outer surface. A carburization test was conducted in a specially designed and manufactured HK-40 alloy tube. Ethylene pyrolysis is considered the most important process in the petrochemical industry for producing petrochemical products. Some furnace tubes used for ethylene pyrolysis often suffer severe high-temperature corrosion since the tube surfaces are heated up to about 1,100 0C in contact with steam-hydrocarbon gas mixtures. Simultaneous carbon deposition on the tube surfaces (i.e. coking) can deteriorate the mechanical properties of the tube materials and may result in a failure of the furnace tubes in the form of carburization or metal dusting. This investigation consists of four separate experimental practices to detect and assess the carburization and metal dusting damage. It involves a) impulse testing to study changes in natural elastic wave frequencies, b) metallographic evaluation, c) resonant ultrasound spectroscopy (RUS), and d) computational modeling to simulate guided wave and ultrasonic phased array technique. The collaboration of the results of these experiments demonstrated the possibility that ultrasonic phased array can offer an efficient and economical practice to determine the remaining services life of the ethylene furnace tubes. The elastic responses (frequency shift and mode shape changes) of the HK-40 alloy tube was studied due to changes in material properties that result from carburization and metal dusting, a severe form of carburization. Natural frequency analysis was conducted as measured at different locations of the HK-40 alloy tube before and after the carburization test. A shift in natural frequencies was observed and is understood to be due to a reduction in shear wave speed in the carburized samples. This shift seems to correlate to the extent of carburization and forms the basis for a new nondestructive evaluation method. Extensive metallographic examination of transverse and longitudinal cross section samples cut out of the HK-40 alloy tube after carburization using optical macrograph, scanning electron microscopy and energy dispersive X-ray were used to quantify the carburization extent as compared to the corresponding shift in natural frequencies. Computational modeling using a finite element analysis program (COMSOL) was used to simulate different scenarios of alternating the material properties, depth and shape of carburization and metal dusting. The simulations revealed strong reflections from relatively high defect depth to tube thickness ratio based on exciting a guided wave. Relatively small defects were very weak in terms of wave reflection amplitude. Hence, phased array technique was utilized in the simulation to enhance the use of guided wave by amplifying the low peak amplitude of the reflected wave from defects. The research reported provides a new approach to advanced nondestructive testing to evaluate the remaining life of ethylene furnace tubes and other application tubes suffering carburization and metal dusting."],"dc:format.medium":["born digital","doctoral dissertations"],"dc:identifier":["T 7847"],"dc:identifier.uri":["https://hdl.handle.net/11124/20149"],"dc:language":["English"],"dc:language.iso":["eng"],"dc:publisher":["Colorado School of Mines. Arthur Lakes Library"],"dc:rights":["Copyright of the original work is retained by the author."],"dc:subject":["metal dusting","carburization","non-destructive examination"],"dc:title":["Investigation of carburization extent from the inner diameter (ID) of ethylene furnace tubes using non-destructive examination (NDE) applied on the outer diameter (OD)"],"dc:type":["Text"],"thesis:degree_discipline":["Metallurgical and Materials Engineering"],"thesis:degree_level":["Doctoral"],"thesis:degree_name":["Doctor of Philosophy (Ph.D.)"],"thesis:institution_name":["Colorado School of Mines"]},"updated_at":"2026-07-24T01:43:42Z"}