Analysis of phase transformations in hydrogenated titanium metals by non-isothermal dilatometry

Hydrogen was used as a temporary alloying element in CP Ti and Ti-6AI-4V. The microstructural evolution and phase transformations were monitored, before, during and after hydrogenation with in-situ dilatometric testing. Wrought CP Ti and Ti-6AI-4V specimens were pre-annealed and experienced four consecutive thermal cycles (Cycles 1-4) i.e. hydrogenation, post-hydrogenation, dehydrogenation and post-dehydrogenation, during dilatometric testing. The specimen in each thermal cycle was heated to 1000°C, heating rate 1°C/min (with an isothermal hold at 1000°C for three hours for hydrogenation and dehydrogenation cycles) and then cooled to room temperature at cooling rate of 1°C/min.

Grantor dc:publisher.institution

Centre for Materials Engineering

Year dc:date.issued

2011

Author dc:creator

• Abbas, Naseeba

Advisor dc:contributor.advisor

• Knutsen, Robert D

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/11427/12339

OAI identifier oai:identifier

oai:open.uct.ac.za:11427/12339