{"id":{"repo_id":"cambridge","oai_identifier":"oai:www.repository.cam.ac.uk:1810/279089"},"canonical_url":"https://search.dev.ndltd.org/etd/cambridge/oai:www.repository.cam.ac.uk:1810/279089","repository":{"repo_id":"cambridge","name":"Cambridge University","base_url":"https://api.repository.cam.ac.uk/server/oai/request"},"display":{"title":"Design of Titania Photocatalytic Membranes containing Fine Ceramic Fibres","abstract":"Photocatalytic membranes have been designed using two types of fine-scale alumina fibres, namely Nano Alumina Fibre (NAF) from Metallurg Engineering, Estonia and commercially available Saffil® Alumina Fibre (SAF) produced by Saffil Limited, UK. NAF fibres have an average diameter of about 15 nm and SAF about 4 μm. Membranes were produced in various ways. The fibre network architecture within the membranes, along with their porosity, specific surface area and mechanical properties, have been examined. These NAF-SAF membranes were impregnated with titania-based sol-gel coatings, to produce photocatalytic membranes. Their mechanical properties, specific surface area and flow properties were assessed and photocatalytic potential was measured by studying rates of degradation of aqueous dye solution. Membranes with photo-active top layers were designed by sedimentation of a fibrous layer of NAF-SAF, containing titania nanoparticles on a pre-sedimented support layer. Two types of photocatalyst were used, one a commercially available anatase nanopowder and the other silver-coated anatase. The latter was produced via modification of the first. Optimisation of the nanoparticle loadings was performed via assessing their photocatalytic efficiency. Specific permeability values were obtained experimentally and by prediction from the pore architecture. A novel form of photo-active membrane was designed by direct casting of milled SAF and titania-based sol-gel into circular moulds. Effects of fibre milling time and fibre to sol-gel ratio on their performance were studied, besides mechanical properties, porosity and specific surface area. Their flow properties and photocatalytic efficiency were also examined. Due to the availability of these fibres, especially the high production rates (kg/h range) and low cost of NAF, these membranes offer potential for large scale application.","abstract_html":"Photocatalytic membranes have been designed using two types of fine-scale alumina fibres, namely Nano Alumina Fibre (NAF) from Metallurg Engineering, Estonia and commercially available Saffil® Alumina Fibre (SAF) produced by Saffil Limited, UK. NAF fibres have an average diameter of about 15 nm and SAF about 4 μm. Membranes were produced in various ways. The fibre network architecture within the membranes, along with their porosity, specific surface area and mechanical properties, have been examined. These NAF-SAF membranes were impregnated with titania-based sol-gel coatings, to produce photocatalytic membranes. Their mechanical properties, specific surface area and flow properties were assessed and photocatalytic potential was measured by studying rates of degradation of aqueous dye solution. Membranes with photo-active top layers were designed by sedimentation of a fibrous layer of NAF-SAF, containing titania nanoparticles on a pre-sedimented support layer. Two types of photocatalyst were used, one a commercially available anatase nanopowder and the other silver-coated anatase. The latter was produced via modification of the first. Optimisation of the nanoparticle loadings was performed via assessing their photocatalytic efficiency. Specific permeability values were obtained experimentally and by prediction from the pore architecture. A novel form of photo-active membrane was designed by direct casting of milled SAF and titania-based sol-gel into circular moulds. Effects of fibre milling time and fibre to sol-gel ratio on their performance were studied, besides mechanical properties, porosity and specific surface area. Their flow properties and photocatalytic efficiency were also examined. Due to the availability of these fibres, especially the high production rates (kg/h range) and low cost of NAF, these membranes offer potential for large scale application.","abstract_has_math":false,"creators":["SHARIF, NASHID"],"institution":"University of Cambridge","degree_name":"Doctor of Philosophy (PhD)","degree_level":"Doctoral","degree_discipline":null,"degree_department":null,"school":null,"contributors":[],"advisors":["Clyne, T W"],"committee_chairs":[],"committee_members":[],"year":2018,"date_issued":"2018-10-20","date_published":"2018-10-20","updated_at":"2026-07-22T22:24:16Z","subjects":["Titania","Photocatalytic","Membrane","Ceramic","Fibre"],"languages":["en"],"rights":[],"rights_urls":["https://apollo8-f-pro.lib.cam.ac.uk/bitstreams/7b2e66de-a263-44f6-ab65-cf6d333b47dc/download","https://www.rioxx.net/licenses/all-rights-reserved/"],"identifier_entries":[]},"links":{"outbound_url":"https://doi.org/10.17863/CAM.26469","outbound_label":"DOI","outbound_source":"dc:identifier.doi"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.advisor","label":"Advisor","values":["Clyne, T W"]},{"key":"dc:contributor.sponsor","label":"Sponsor","values":["IDB-Cambridge Commonwealth, European and International Trust (IDB-CCEIT), Metallurg Engineering, Fitzwilliam College and Charles Wallace Bangladesh Trust"]},{"key":"dc:creator","label":"Author","values":["SHARIF, NASHID"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.issued","label":"Date","values":["2018-10-20"]},{"key":"dc:publisher.institution","label":"Dc Publisher Institution","values":["University of Cambridge"]},{"key":"dc:relation.isreferencedby.uri","label":"Dc Relation Isreferencedby URI","values":["https://www.repository.cam.ac.uk/handle/1810/279089"]},{"key":"dc:type","label":"Dc Type","values":["Thesis"]},{"key":"dc:type.qualificationlevel","label":"Dc Type Qualificationlevel","values":["Doctoral"]},{"key":"dc:type.qualificationname","label":"Dc Type Qualificationname","values":["Doctor of Philosophy (PhD)"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Titania","Photocatalytic","Membrane","Ceramic","Fibre"]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["en"]},{"key":"dc:rights","label":"Dc Rights","values":["https://apollo8-f-pro.lib.cam.ac.uk/bitstreams/7b2e66de-a263-44f6-ab65-cf6d333b47dc/download","https://www.rioxx.net/licenses/all-rights-reserved/"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.doi","label":"DOI","values":["10.17863/CAM.26469"]},{"key":"dc:identifier.uri","label":"Identifier URI","values":["https://apollo8-f-pro.lib.cam.ac.uk/bitstreams/f45c3016-5ae9-4489-95e0-960aac68e21f/download"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["Photocatalytic membranes have been designed using two types of fine-scale alumina fibres, namely Nano Alumina Fibre (NAF) from Metallurg Engineering, Estonia and commercially available Saffil® Alumina Fibre (SAF) produced by Saffil Limited, UK. NAF fibres have an average diameter of about 15 nm and SAF about 4 μm. Membranes were produced in various ways. The fibre network architecture within the membranes, along with their porosity, specific surface area and mechanical properties, have been examined. These NAF-SAF membranes were impregnated with titania-based sol-gel coatings, to produce photocatalytic membranes. Their mechanical properties, specific surface area and flow properties were assessed and photocatalytic potential was measured by studying rates of degradation of aqueous dye solution. Membranes with photo-active top layers were designed by sedimentation of a fibrous layer of NAF-SAF, containing titania nanoparticles on a pre-sedimented support layer. Two types of photocatalyst were used, one a commercially available anatase nanopowder and the other silver-coated anatase. The latter was produced via modification of the first. Optimisation of the nanoparticle loadings was performed via assessing their photocatalytic efficiency. Specific permeability values were obtained experimentally and by prediction from the pore architecture. A novel form of photo-active membrane was designed by direct casting of milled SAF and titania-based sol-gel into circular moulds. Effects of fibre milling time and fibre to sol-gel ratio on their performance were studied, besides mechanical properties, porosity and specific surface area. Their flow properties and photocatalytic efficiency were also examined. Due to the availability of these fibres, especially the high production rates (kg/h range) and low cost of NAF, these membranes offer potential for large scale application."]},{"key":"dc:format.checksum.md5","label":"Dc Format Checksum Md5","values":["87eda9de84448d1f82354d60eee3eb5f","95b9e577f28d7afa46cdbd3cfc0cfe7e"]},{"key":"dc:title","label":"Title","values":["Design of Titania Photocatalytic Membranes containing Fine Ceramic Fibres"]}]}],"canonical_facts":{"dc:contributor.advisor":["Clyne, T W"],"dc:contributor.sponsor":["IDB-Cambridge Commonwealth, European and International Trust (IDB-CCEIT), Metallurg Engineering, Fitzwilliam College and Charles Wallace Bangladesh Trust"],"dc:creator":["SHARIF, NASHID"],"dc:date.issued":["2018-10-20"],"dc:description.abstract":["Photocatalytic membranes have been designed using two types of fine-scale alumina fibres, namely Nano Alumina Fibre (NAF) from Metallurg Engineering, Estonia and commercially available Saffil® Alumina Fibre (SAF) produced by Saffil Limited, UK. NAF fibres have an average diameter of about 15 nm and SAF about 4 μm. Membranes were produced in various ways. The fibre network architecture within the membranes, along with their porosity, specific surface area and mechanical properties, have been examined. These NAF-SAF membranes were impregnated with titania-based sol-gel coatings, to produce photocatalytic membranes. Their mechanical properties, specific surface area and flow properties were assessed and photocatalytic potential was measured by studying rates of degradation of aqueous dye solution. Membranes with photo-active top layers were designed by sedimentation of a fibrous layer of NAF-SAF, containing titania nanoparticles on a pre-sedimented support layer. Two types of photocatalyst were used, one a commercially available anatase nanopowder and the other silver-coated anatase. The latter was produced via modification of the first. Optimisation of the nanoparticle loadings was performed via assessing their photocatalytic efficiency. Specific permeability values were obtained experimentally and by prediction from the pore architecture. A novel form of photo-active membrane was designed by direct casting of milled SAF and titania-based sol-gel into circular moulds. Effects of fibre milling time and fibre to sol-gel ratio on their performance were studied, besides mechanical properties, porosity and specific surface area. Their flow properties and photocatalytic efficiency were also examined. Due to the availability of these fibres, especially the high production rates (kg/h range) and low cost of NAF, these membranes offer potential for large scale application."],"dc:format.checksum.md5":["87eda9de84448d1f82354d60eee3eb5f","95b9e577f28d7afa46cdbd3cfc0cfe7e"],"dc:identifier.doi":["10.17863/CAM.26469"],"dc:identifier.uri":["https://apollo8-f-pro.lib.cam.ac.uk/bitstreams/f45c3016-5ae9-4489-95e0-960aac68e21f/download"],"dc:language":["en"],"dc:publisher.institution":["University of Cambridge"],"dc:relation.isreferencedby.uri":["https://www.repository.cam.ac.uk/handle/1810/279089"],"dc:rights":["https://apollo8-f-pro.lib.cam.ac.uk/bitstreams/7b2e66de-a263-44f6-ab65-cf6d333b47dc/download","https://www.rioxx.net/licenses/all-rights-reserved/"],"dc:subject":["Titania","Photocatalytic","Membrane","Ceramic","Fibre"],"dc:title":["Design of Titania Photocatalytic Membranes containing Fine Ceramic Fibres"],"dc:type":["Thesis"],"dc:type.qualificationlevel":["Doctoral"],"dc:type.qualificationname":["Doctor of Philosophy (PhD)"]},"updated_at":"2026-07-22T22:24:16Z"}