description: The focus of this work is to investigate the dissolution of MW25, a non-radioactive simulant of UK high-level nuclear waste borosilicate glass, and to predict its performance in the near field of a geological repository. A single-pass flow-through (SPFT) experimental system was used to measure the forward dissolution rates of MW25. Experiments were conducted in two parts. Experiment Part 1 considers the dissolution of the waste glass in deionised water at 40 and 90 oC and circum-neutral pH. Experiment Part 2 considers the dissolution of the waste glass in simulant groundwaters, with similar compositions to groundwaters of Callovo-Oxfordian clay (lower-strength sedimentary rock (LSSR)) and Borrowdale Volcanic Group rocks (higher-strength rock (HSR)), at 40 oC and pH 7. The forward dissolution rate measured in deionised water was found to be approximately one order of magnitude higher at 90 oC than at 40 oC. A similar release was observed for Si, Mg and Al at 40 oC and 90 oC, whereas the B, Cs, Na, Li and Mo showed an order of magnitude increase when the temperature was increased from 40 to 90 oC for low q/S values. The activation energy (Ea) of the reactions shows that the dissolution process is a surface phenomenon. At 90 oC the net effect of the processes governing MW25 dissolution led to the preferential release of boron and alkali metals relative to the release of Si during the transient dissolution stage, accompanied by an increase in the concentration of silicic acid. This suggests that the solution activity of silicic acid at a higher temperature has a weak influence on the release of the mobile elements. The forward dissolution rate measured in LSSR simulant groundwater was found to be slightly higher than that measured in HSR simulant groundwater. The dissolution behaviour of MW25 in both groundwaters is consistent with its behaviour in deionised water at 40 oC, with the dissolution rates of elements increasing as flow rates were increased. However, forward …
abstract: The focus of this work is to investigate the dissolution of MW25, a non-radioactive simulant of UK high-level nuclear waste borosilicate glass, and to predict its performance in the near field of a geological repository. A single-pass flow-through (SPFT) experimental system was used to measure the forward dissolution rates of MW25. Experiments were conducted in two parts. Experiment Part 1 considers the dissolution of the waste glass in deionised water at 40 and 90 oC and circum-neutral pH. Experiment Part 2 considers the dissolution of the waste glass in simulant groundwaters, with similar compositions to groundwaters of Callovo-Oxfordian clay (lower-strength sedimentary rock (LSSR)) and Borrowdale Volcanic Group rocks (higher-strength rock (HSR)), at 40 oC and pH 7. The forward dissolution rate measured in deionised water was found to be approximately one order of magnitude higher at 90 oC than at 40 oC. A similar release was observed for Si, Mg and Al at 40 oC and 90 oC, whereas the B, Cs, Na, Li and Mo showed an order of magnitude increase when the temperature was increased from 40 to 90 oC for low q/S values. The activation energy (Ea) of the reactions shows that the dissolution process is a surface phenomenon. At 90 oC the net effect of the processes governing MW25 dissolution led to the preferential release of boron and alkali metals relative to the release of Si during the transient dissolution stage, accompanied by an increase in the concentration of silicic acid. This suggests that the solution activity of silicic acid at a higher temperature has a weak influence on the release of the mobile elements. The forward dissolution rate measured in LSSR simulant groundwater was found to be slightly higher than that measured in HSR simulant groundwater. The dissolution behaviour of MW25 in both groundwaters is consistent with its behaviour in deionised water at 40 oC, with the dissolution rates of elements increasing as flow rates were increased. However, forward …
author: Iwalewa, Tajudeen
language: en
keywords: MW25, borosilicate glass, nuclear waste, geological repository, radionuclide, dissolution, temperature, flow rate, UK, GoldSim, reactive transport, modelling, surface area, disposal option, aqueous geochemistry, SEM, EDX, XRD, single-pass flow-through, SPFT, environmental impact, performance assessment, LSSR, HSR, Callovo-Oxfordian clay, Borrowdale Volcanic Group rock, high-level waste, HLW, ion exchange, hydrolysis, forward dissolution rate
license: https://apollo8-f-pro.lib.cam.ac.uk/bitstreams/527b9722-fba1-43f9-8a26-23adf3bda483/download
license: https://www.rioxx.net/licenses/all-rights-reserved/
date published: 2017-05-01
date modified: 2026-07-22T22:24:28Z
provider: Cambridge University
publisher: Networked Digital Library of Theses and Dissertations
type: WebPage
source organization: University of Cambridge

PropertyValue
property ID: DOI
value: 10.17863/CAM.11803