{"id":{"repo_id":"brazil-uerj","oai_identifier":"oai:pantheon.ufrj.br:11422/6543"},"canonical_url":"https://search.dev.ndltd.org/etd/brazil-uerj/oai:pantheon.ufrj.br:11422/6543","repository":{"repo_id":"brazil-uerj","name":"Brazil UERJ","base_url":"https://pantheon.ufrj.br/oai/request"},"display":{"title":"Avaliação da resistência mecânica e da molhabilidade de fibras de aramida após tratamento com plasma de argônio","abstract":"This work presents the analysis of mechanical strength, wettability and the surface of aramid fiber treated with argon plasma. The fiber was treated with argon plasma with a vacuum of 8x10-1 bar with power of 50 and 100 Watts, and, for each voltage, tests were carried out with duration of 1, 3 and 5 minutes. The tests performed were tensile tests, tensiometry and scanning electron microscopy (SEM) By analyzing the results, it was observed that, for the 100 Watt treatment, the fiber presented an improvement in its wettability and an increase of 47% in the fiber’s strength resistance for the treatment duration of 3 minutes and, for the duration of 5 minutes, it is noticed that the value of the strength resistance begins to decay. The plasma treatment also increased the roughness of the fiber surface and caused the inclusion of incrustations on it, indicating a possible improvement in the mechanical interlock between fiber and matrix.","abstract_html":"This work presents the analysis of mechanical strength, wettability and the surface of aramid fiber treated with argon plasma. The fiber was treated with argon plasma with a vacuum of 8x10-1 bar with power of 50 and 100 Watts, and, for each voltage, tests were carried out with duration of 1, 3 and 5 minutes. The tests performed were tensile tests, tensiometry and scanning electron microscopy (SEM) By analyzing the results, it was observed that, for the 100 Watt treatment, the fiber presented an improvement in its wettability and an increase of 47% in the fiber’s strength resistance for the treatment duration of 3 minutes and, for the duration of 5 minutes, it is noticed that the value of the strength resistance begins to decay. The plasma treatment also increased the roughness of the fiber surface and caused the inclusion of incrustations on it, indicating a possible improvement in the mechanical interlock between fiber and matrix.","abstract_has_math":false,"creators":["Santos, Mariana Oliveira"],"institution":"Universidade Federal do Rio de Janeiro","degree_name":null,"degree_level":null,"degree_discipline":null,"degree_department":null,"school":null,"contributors":[],"advisors":["Simão, Renata Antoun"],"committee_chairs":[],"committee_members":[],"year":2017,"date_issued":"2017-04","date_published":"2017-04","updated_at":"2026-07-24T01:16:21Z","subjects":["Engenharia metalúrgica e de materiais","Fibras de aramida x avaliação."],"languages":["por"],"rights":["Acesso Aberto"],"rights_urls":[],"identifier_entries":[]},"links":{"outbound_url":"http://hdl.handle.net/11422/6543","outbound_label":"Handle","outbound_source":"dc:identifier.uri"},"metadata_groups":[{"id":"people","label":"People","entries":[{"key":"dc:contributor.advisor","label":"Advisor","values":["Simão, Renata Antoun"]},{"key":"dc:creator","label":"Author","values":["Santos, Mariana Oliveira"]}]},{"id":"academic_context","label":"Academic Context","entries":[{"key":"dc:date.accessioned","label":"Dc Date Accessioned","values":["2019-02-19T12:41:06Z"]},{"key":"dc:date.available","label":"Dc Date Available","values":["2026-05-16T03:04:54Z"]},{"key":"dc:date.issued","label":"Date","values":["2017-04"]},{"key":"dc:publisher","label":"Institution","values":["Universidade Federal do Rio de Janeiro"]},{"key":"dc:publisher.department","label":"Dc Publisher Department","values":["Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia"]},{"key":"dc:type","label":"Dc Type","values":["Dissertação"]}]},{"id":"subjects_keywords","label":"Subjects and Keywords","entries":[{"key":"dc:subject","label":"Dc Subject","values":["Engenharia metalúrgica e de materiais","Fibras de aramida x avaliação."]}]},{"id":"language_rights","label":"Language and Rights","entries":[{"key":"dc:language","label":"Dc Language","values":["por"]},{"key":"dc:rights","label":"Dc Rights","values":["Acesso Aberto"]}]},{"id":"identifiers","label":"Identifiers","entries":[{"key":"dc:identifier.uri","label":"Identifier URI","values":["http://hdl.handle.net/11422/6543"]}]},{"id":"additional","label":"Additional Metadata","entries":[{"key":"dc:description.abstract","label":"Abstract","values":["This work presents the analysis of mechanical strength, wettability and the surface of aramid fiber treated with argon plasma. The fiber was treated with argon plasma with a vacuum of 8x10-1 bar with power of 50 and 100 Watts, and, for each voltage, tests were carried out with duration of 1, 3 and 5 minutes. The tests performed were tensile tests, tensiometry and scanning electron microscopy (SEM) By analyzing the results, it was observed that, for the 100 Watt treatment, the fiber presented an improvement in its wettability and an increase of 47% in the fiber’s strength resistance for the treatment duration of 3 minutes and, for the duration of 5 minutes, it is noticed that the value of the strength resistance begins to decay. The plasma treatment also increased the roughness of the fiber surface and caused the inclusion of incrustations on it, indicating a possible improvement in the mechanical interlock between fiber and matrix."]},{"key":"dc:title","label":"Title","values":["Avaliação da resistência mecânica e da molhabilidade de fibras de aramida após tratamento com plasma de argônio"]}]}],"canonical_facts":{"dc:contributor.advisor":["Simão, Renata Antoun"],"dc:creator":["Santos, Mariana Oliveira"],"dc:date.accessioned":["2019-02-19T12:41:06Z"],"dc:date.available":["2026-05-16T03:04:54Z"],"dc:date.issued":["2017-04"],"dc:description.abstract":["This work presents the analysis of mechanical strength, wettability and the surface of aramid fiber treated with argon plasma. The fiber was treated with argon plasma with a vacuum of 8x10-1 bar with power of 50 and 100 Watts, and, for each voltage, tests were carried out with duration of 1, 3 and 5 minutes. The tests performed were tensile tests, tensiometry and scanning electron microscopy (SEM) By analyzing the results, it was observed that, for the 100 Watt treatment, the fiber presented an improvement in its wettability and an increase of 47% in the fiber’s strength resistance for the treatment duration of 3 minutes and, for the duration of 5 minutes, it is noticed that the value of the strength resistance begins to decay. The plasma treatment also increased the roughness of the fiber surface and caused the inclusion of incrustations on it, indicating a possible improvement in the mechanical interlock between fiber and matrix."],"dc:identifier.uri":["http://hdl.handle.net/11422/6543"],"dc:language":["por"],"dc:publisher":["Universidade Federal do Rio de Janeiro"],"dc:publisher.department":["Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia"],"dc:rights":["Acesso Aberto"],"dc:subject":["Engenharia metalúrgica e de materiais","Fibras de aramida x avaliação."],"dc:title":["Avaliação da resistência mecânica e da molhabilidade de fibras de aramida após tratamento com plasma de argônio"],"dc:type":["Dissertação"]},"updated_at":"2026-07-24T01:16:21Z"}