Evaluation of the critical parameters and polymeric coat performance in compressed multiparticulate systems
type: CreativeWork
description: Compression of coated pellets is a practical alternative to capsule filling. The current practice is to add cushioning agents to minimize the stress on the coated pellets. Cushioning agents however add bulkiness and reduce the overall drug loading capacity. In this study, we investigated the performance of compressed coated pellets with no cushioning agent to evaluate the feasibility of predicting the coat behaviour using thermo-mechanical and rheological analysis techniques. Different coating formulations were made of ethyl cellulose (EC) as a coating polymer and two different kinds of additives were incorporated into the polymeric coating solution. Triethyl Citrate (TEC) and Polyethylene glycol 400(PEG400) were used as plasticizers at different levels to the coating formulations (10%, 20%, 30%). Thermal, mechanical and rheological measurements of the coating film formulations were achieved to investigate the effect of plasticizers. Thermal gravimetric analysis results (TGA) showed higher residual moisture content in films plasticised with PEG 400 compared to their TEC counterparts. Differential Scanning Calorimetry (DSC), Dynamic Mechanical Analysis (DMA) and Parallel Plate Shear Rheometer (PPSR) were used to study the influence of the level and type of plasticisers incorporated in coating film formulation on the performance of the coating film. In this study, both DSC and DMA were used to investigate the Tg for each film coating formulation in order to evaluate the effect of the additives. In general DMA results for the Tg value of the films were always higher by 10-20% than those measured by the DSC. Furthermore, clamp size and the frequency of the oscillation have an influence on the evaluation of Tg. Complex viscosity for different coating film formulations revealed that the shear hinning gradient changes with temperature and plasticiser type and concentration. The value of complex viscosity from DMA and PPSR exhibits power law behaviour. The rheological modul…
abstract: Compression of coated pellets is a practical alternative to capsule filling. The current practice is to add cushioning agents to minimize the stress on the coated pellets. Cushioning agents however add bulkiness and reduce the overall drug loading capacity. In this study, we investigated the performance of compressed coated pellets with no cushioning agent to evaluate the feasibility of predicting the coat behaviour using thermo-mechanical and rheological analysis techniques. Different coating formulations were made of ethyl cellulose (EC) as a coating polymer and two different kinds of additives were incorporated into the polymeric coating solution. Triethyl Citrate (TEC) and Polyethylene glycol 400(PEG400) were used as plasticizers at different levels to the coating formulations (10%, 20%, 30%). Thermal, mechanical and rheological measurements of the coating film formulations were achieved to investigate the effect of plasticizers. Thermal gravimetric analysis results (TGA) showed higher residual moisture content in films plasticised with PEG 400 compared to their TEC counterparts. Differential Scanning Calorimetry (DSC), Dynamic Mechanical Analysis (DMA) and Parallel Plate Shear Rheometer (PPSR) were used to study the influence of the level and type of plasticisers incorporated in coating film formulation on the performance of the coating film. In this study, both DSC and DMA were used to investigate the Tg for each film coating formulation in order to evaluate the effect of the additives. In general DMA results for the Tg value of the films were always higher by 10-20% than those measured by the DSC. Furthermore, clamp size and the frequency of the oscillation have an influence on the evaluation of Tg. Complex viscosity for different coating film formulations revealed that the shear hinning gradient changes with temperature and plasticiser type and concentration. The value of complex viscosity from DMA and PPSR exhibits power law behaviour. The rheological modul…
author: Benhadia, Abrehem M.A.
language: en
keywords: Ethyl cellulose films, Plasticisers, TGA, DSC, DMA, Shear rheometry, Glass transition temperature, Extrusion-spheronisation, Film coating, Direct compression, Scanning electron microscopy, Statistical analysis, Quality by design, Dissolution
date modified: 2026-07-24T01:14:55Z
provider: University of Bradford
publisher: Networked Digital Library of Theses and Dissertations
type: WebPage
source organization: University of Bradford

PropertyValue
property ID: Handle
value: http://hdl.handle.net/10454/17459