  1. Charakterizace žárově stříkaného kovokeramického WC-CoCr povlaku na hořčíkové slitině AZ91

    Horáková, LenkaVysoké učení technické v Brně. Fakulta chemická

    … WC-CoCr povlaku na hořčíkové slitině AZ91 z hlediska mikrostruktury, chemického a fázového složení a mechanických vlastností. Depozice byla provedena metodou HVOF (High Velocity Oxy-Fuel). Teoretická část je věnována hořčíkovým slitinám se zaměřením na slitinu AZ91. Dále je v …

    brno-tech Repository record

  2. Biodegradable stents made of pure Mg and AZ91 alloy through SPS sintering

    de Oliveira Botelho, Pedro AugustoUniversità degli studi di Trento2015

    … from the powder is investigated. Pure Mg and the AZ91 Mg powders were used in the present study. Pure Mg powder was sintered by Spark Plasma Sintering at 400 and 470 °C, and the AZ91 powder was sintered at 400 °C without homogenization and at 470 °C after homogenization. The preforms produced by …

    trento Repository record

  3. Hot workability of magnesium alloys

    Mwembela, Aaron Absalom1997

    For the alloy AZ91 (Mg-9.OAl-0.7Zn-0.13Mn) die cast specimens were subjected to torsion testing at 150, 180, 240, 300, 420 and 450C̕ at 0.05 0.5 and 5.0 s -1 The as-cast specimens exhibited hot shortness at 360C̕ and above; however in that domain, after prior thermomechanical processing (TMP) at …

    concordia Repository record

  4. Cerium-based conversion coatings on magnesium alloys

    Castaño, Carlos E.Missouri University of Science and Technology2016

    … conversion coatings (CeCCs) on AZ31B and AZ91D Mg alloys. Deposition of homogenous and protective CeCCs was highly dependent on the surface preparation steps. The best results were obtained when Mg samples underwent grinding, acid cleaning, and alkaline cleaning processes. This reduced the …

    must-thes Repository record

  5. The Effects of Laser Shock Peening on the Residual Stress and Corrosion Characteristics of Magnesium Alloy AZ91D for use as Biodegradable Implants

    Russo, JamesUniversity of Cincinnati2012

    … the corrosion characteristics of magnesium alloy AZ91D. In order to understand all aspects of this, an in-depth material characterization of the alloy is performed. Next, an LSP study is performed in which the optimal LSP parameters are determined. The experimental results are validated using …

    ohiolink Repository record