The mechanism of corrosion of cadmium-silver-copper bearing alloys

Tests were made at the Lubrication Laboratory at Virginia Polytechnic Institute to determine the mechanism of corrosion of Cadmium-Silver-Copper bearing metals, and if possible to develop a procedure to quantitatively rate oils and inhibitors with respect to corrosion. Two pieces of testing apparatus were employed - a jet-type oil bath and a glass apparatus. It was found that corrosion of the cadmium base bearing metals took place in the jet-type oil bath with jet velocities equal to 1.51 feet per second at temperatures of 300 and 325° F with Esso Motor Oil, No. 3. Corrosion did not take place at temperatures of 300 and 325° F in the jet-type oil bath when the jet velocities were decreased to 0.67 feet per second. Tests on the glass apparatus indicated that the corrosion was not electrolytic, that the presence of air (oxygen) at the oil-bearing interface was necessary for corrosion to proceed, and that the scrubbing action of the oil past the bearing face only partially influences the rate of corrosion. The jet-type apparatus is believed to be quantitative in its results if the surface condition of the bearing specimens and the velocity of the issuing oil jets are accurately controlled. Viscosity of the oil prior to and after the test was measured. No consistent trend of viscosity was noted, but a tendency for the viscosity of the oil to be directly proportional to the total weight of metal lost by corrosion was pointed out.

Name thesis:degree_name

M.S.

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Chemical Engineering

Department dc:contributor.department

Chemical Engineering

Grantor dc:publisher

Virginia Agricultural and Mechanical College and Polytechnic Institute

Year dc:date.issued

1937

Author dc:creator

• Hoskins, Robert Joseph

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en_US

Handle dc:identifier.uri

http://hdl.handle.net/10919/94457

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/94457