Temperature Dependent Behavior of Optical Loss from Hydrogen Species in Optical Fibers at High Temperature

This study reports on the behavior of silica based optical fibers in a hydrogen environment at high temperatures. The hydrogen response in the form of optical loss in the wavelength range of 1000-2500 nm of a germanium doped graded index 50/125 graded index fiber was examined in the temperature range of 20–800 °C. When the fiber was exposed to hydrogen at 800 °C two absorption bands appeared: ~1390 nm assigned to the first overtone of the hydroxyl stretch and ~2200 nm band with complex assignments including the combination mode of the fundamental hydroxyl stretch with SiO4 tetrahedral vibrations and the combination mode of SiOH bend and stretch. The growth rate of the 1390 nm band fits the solution to the diffusion equation in cylindrical coordinates while the 2200 nm band does not. Absorption for both bands persisted as the fiber is cooled to room temperature. Temperature dependent behavior was observed in that as temperature increases from room temperature, the absorption intensity decreases and band shifts slightly to longer wavelengths. Temperature dependence is repeatable and reversible. However, if no hydrogen is present in the environment at temperatures greater than 700 °C, the 1390 nm band will permanently decrease in intensity, while the 2200 nm band does not change. Changes in the structure of the glass appear to be causing this temperature dependent behavior. Other necessary conditions for structural changes to cause this temperature dependent behavior are examined.

Name thesis:degree_name

Master of Science

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Materials Science and Engineering

Department dc:contributor.department

Materials Science and Engineering

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2015

Author dc:creator

• Bonnell, Elizabeth Ann

Chair dc:contributor.committeechair

• Pickrell, Gary R.

Committee members dc:contributor.committeemember

• Homa, Daniel S.
• Winkler, Christopher

• Infrared Spectroscopy
• Diffusion
• Glass Structure
• OH Species
• Temperature Dependence
• Fiber Optics
• Hydrogen

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en_US

Dc Identifier Other

etd-05202015-113311

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/78132