The effect of diffused hydrogen on the torsional fatigue life of 2024-T351 aluminum alloy

Fatigue tests in reversed torsion were run on 2024-T351 aluminum alloy specimens into which hydrogen had been diffused. The diffusion was accomplished by placing the specimens in a hydrogen environment (>99.5%) for 25 days at 2000 psi [13.8 MPa] and 123°C. A control group was tested which underwent the same temperature conditions for 25 days. The fatigue tests were run at low (20-25%) and high (85-90%) relative humidities and at shear stress levels of approximately 13400, 16800, and 20100 psi [89.6, 117, and 138 MPa]. The results of this investigation show that hydrogen charging has no effect on the torsional fatigue life of aluminum. However, a change in the crack propagation angle at high relative humidity for a ductile, circumferential crack on uncharged specimens to a brittle, 45° crack on hydrogen-charged specimens may be the result of hydrogen embrittlement.

Name thesis:degree_name

Master of Science

Level thesis:degree_level

masters

Discipline thesis:degree_discipline

Mechanical Engineering

Department dc:contributor.department

Mechanical Engineering

Grantor dc:publisher

Virginia Polytechnic Institute and State University

Year dc:date.issued

1978

Author dc:creator

• Kauffmann, Charles Joseph

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en

Handle dc:identifier.uri

http://hdl.handle.net/10919/64657

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/64657