Moisture and stress effects on fretting between steel and polyimide coatings

Fretting of solvent cast polyimide coatings was investigated in a ball-on-flat geometry as a function of relative humidity. Polyimides were synthesized from benzophenone tetracarboxylic dianhydride (BTDA) and bisanline (Bis P), 6-fluoro bis dian hydride (6FDA) and Bis P, and pyromellitic dianhydride (PMDA) and bis A phenyl phosphine oxide (BAPPO). Coating life - the time for the steel ball to wear through the coating - shortened with increasing humidity. Iron oxides or other reaction products from 52100 ball generated at high humidity acted as abrasives and accelerated the wear of the coatings. Variation of coating life among the three polyimides was attributed to the residual stress, which developed upon cooling from the annealing temperature due to the mismatch of thermal expansion coefficients between the polymer and the metal substrate. Calculated from elasticity theory, the normal stress dropped shortly after the start of the test, remained relatively constant, and increased toward the end. This variation correlated with the wear rate and accounted for the non-linear increase of coating life with coating thickness. Sub-surface shear stress and surface tensile stress predicted well, respectively, the debonded shape and the inter-crack spacing of Hertzian cracks.

Name thesis:degree_name

Ph. D.

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Materials Engineering Science

Department dc:contributor.department

Materials Engineering Science

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

1993

Author dc:creator

• Kang, Chiun-Chia

Chair dc:contributor.committeechair

• Eiss, Norman S. Jr.

Committee members dc:contributor.committeemember

• Furey, Michael J.
• Ward, Thomas C.
• Wightman, James P.
• Wilkes, Garth L.

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Language dc:language.iso

en

Dc Identifier Other

etd-06062008-171727

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/38491