Inter-Relationships Between Chemistry, Network Structure and Properties of Chain Growth Dimethacrylate Thermosets

Dimethacrylate oligomers diluted with styrene reactive diluents (so-called vinyl ester resins) are becoming increasingly important for composites in applications such as transportation vehicles, printed wiring boards and civil infrastructure. This research has focused on the generation and comparative analysis of glassy dimethacrylate networks as a function of oligomer structure, the type of reactive diluent, composition and curing conditions. A novel cycloaliphatic dimethacrylate was synthesized and its networks were compared to oligomeric structures containing dimethacrylates derived from epoxy terminated oligomers (from bisphenol-A and epichlorohydrin). Both types of dimethacrylates co-cured with methyl methacrylate exhibited increases in Mc and fracture toughness as the concentration of methyl methacrylate was increased. By contrast, networks prepared with a styrene diluent displayed reduced toughness with increasing styrene and Mc. Due to the need for long-term composite environmental durability, the effects of moisture and exposure to sunlight are important. Thus, these materials were exposed to ultraviolet light on a rotating drum for 225 days and the exposure was carefully monitored. Initial results from this study suggest that both the networks comprising the aromatic dimethacrylate/styrene structures as well as the cycloaliphatic analogues cured with methyl methacrylate undergo reductions in rubbery moduli upon aging under these conditions. X-Ray photoelectron spectroscopy shows higher levels of oxidation on the bisphenol-A vinyl ester networks cured with styrene, especially those containing dimethylaniline and cobalt naphthenate as accelerators. Scanning electron microscopy indicates a smooth surface for the cycloaliphatic networks cured with methyl methacrylate and a pitted surface for the aromatic networks cured with styrene. Water absorption is also higher for the cycloaliphatic vinyl ester; however, curing with a longer alkyl chain methacrylate (butyl methacrylate) decreases the water absorption to levels comparable to those cured with styrene.

Name thesis:degree_name

Ph. D.

Level thesis:degree_level

doctoral

Discipline thesis:degree_discipline

Chemistry

Department dc:contributor.department

Chemistry

Grantor dc:publisher

Virginia Tech

Year dc:date.issued

2001

Author dc:creator

• Starr, Brian Craig

Chair dc:contributor.committeechair

• Riffle, Judy S.

Committee members dc:contributor.committeemember

• Lesko, John J.
• Wightman, James P.
• Shultz, Allan R.
• McGrath, James E.

• fracture toughness
• aliphatic vinyl ester
• dimethacrylate
• water absorption
• accelerated UV aging

Statement dc:rights

• In Copyright

Licence dc:rights.uri

• http://rightsstatements.org/vocab/InC/1.0/

Dc Identifier Other

etd-12062001-080749

OAI identifier oai:identifier

oai:vtechworks.lib.vt.edu:10919/29949