Deformation mechanisms in rapidly solidified aluminum alloys

The deformation mechanisms of four rapidly solidified (RS) and hot extruded aluminum alloys were investigated. Al-8.8Fe-3.7Ce (all compositions in wt%) and Al-8.9Fe-6.9Ce alloys produced from RS powders and two Al-8Fe-2Mo alloys one produced from RS ribbons and the other from powders, respectively, were creep tested in the temperature range 250$\sp\circ$C to 350$\sp\circ$C over a range of stresses from 15 to 250 MPa.

Name thesis:degree_name

Ph.D.

Level thesis:degree_level

Dissertation

Discipline thesis:degree_discipline

Metallurgical Engineering

Grantor

University of Illinois at Urbana-Champaign

Year dc:date

2011

Author dc:creator

• Legzdina, Daira

Contributors dc:contributor

• Fraser, Hamish L.

• Engineering, Metallurgy
• Engineering, Materials Science

Statement dc:rights

• Copyright 1989 Legzdina, Daira

Language dc:language

eng

Identifier

AAI9010929
(UMI)AAI9010929

OAI identifier oai:identifier

oai:www.ideals.illinois.edu:2142/22045