Lattice mismatched epitaxy of heterostructures for non-nitride green light emitting devices

In this project, we implement modern metal organic chemical vapor deposition (MOCVD) technology to fabricate monolithic platforms which integrate traditionally incompatible materials with the ultimate goal of achieving high brightness green to amber light emitting diodes (LEDs) and laser diodes (LDs). Unconventional compositions of aluminum indium gallium phosphide (AlInGaP), with lattice constants less than that of GaAs, offer improved electrical and optical characteristics over commonly used GaAsmatched material. Also, integration of optical III-V material on the CMOS platform has long been a technological goal, and these compositions of AlInGaP are amenable to monolithic integration on the (100) Si platform. In this thesis, we pioneer technology to integrate high quality, novel AlInGaP alloys on III-V substrates (and elsewhere, this technology is successfully extended for III-V integration on (100) Si). We first focus on creating a virtual substrate upon which any lattice constant intermediate to GaAs and GaP is available. Large amounts of lattice mismatch are ultimately relaxed through incremental introduction of strain in compositionally graded epitaxial layers, thus breaking the typical lattice-matched constraint of semiconductor systems. Tensile relaxed gallium arsenide phosphide (GaAsP) graded layers yield virtual substrates with extremely low threading defect densities ([rho]t=104cm-2), while extremely thin, 1.3[mu]m compressively graded GaAsP buffers also yield low thread densities ([rho]t=105cm-2). The lack of phase separation defects along with the atomically smooth nature of the tensile films leads to suppression of dislocation nucleation and efficient dislocation glide which together facilitate complete strain relaxation with minimal escalation of [rho]t.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Materials Science and Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2008

Author dc:creator

• Mori, Michael James

Advisor dc:contributor.advisor

• Eugene A. Fitzgerald.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/44198

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/44198