Microfabrication methods to improve the kinetics of the yttria stabilized zirconia -- platinum -- oxygen electrode

Solid oxide fuel cells are a potential electrical power source that is silent, efficient, modular, and capable of operating on a wide variety of fuels. Unfortunately, current technologies are severely limited in that they provide sufficient power output only at very high temperatures (>800°C). One reason for this is because the electrodes have very poor (and poorly understood) kinetics. The work described in this dissertation involves the microfabrication of model systems with triple phase boundary lengths that varied over an order of magnitude to systematically quantify and ultimately improve the kinetics of platinum electrodes on the surface of yttria stabilized zirconia electrolytes. Platinum electrodes with well controlled geometry were sputtered onto the surface of bulk YSZ and onto sputtered YSZ thin films. An unexpected result was found whereby YSZ films of composition Y0.09Zr0.91O2-x had an ionic conductivity remarkably enhanced by a factor of 20-30. This is attributed to the films exhibiting nanometric grain sizes and thereby stabilizing the cubic morphology at considerably lower yttrium levels than is normally needed. This metastable cubic phase is suspected of having reduced defect ordering.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Materials Science and Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2006

Author dc:creator

• Hertz, Joshua L. (Joshua Lee)

Advisor dc:contributor.advisor

• Harry L. Tuller.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/37354

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/37354