Effects of doping single and double walled carbon nanotubes with nitrogen and boron

Controlling the diameter and chirality of carbon nanotubes to fine tune their electronic band gap will no longer be enough to satisfy the growing list of characteristics that future carbon nanotube applications are starting to require. Controlling their band gap, wall reactivity and mechanical properties is imperative to make them functional. The solution to these challenges is likely to lie in smart defect engineering. Defects of every kind can induce significant changes on the intrinsic properties of carbon nanotubes. In this context, this thesis analyzes the effects of doping single and double walled carbon nanotubes with nitrogen and boron. We describe the synthesis of N-doped single-walled carbon nanotubes (N-SWNTs), that agglomerate in bundles and form long strands (<10cm), via the thermal decomposition of ferrocene/ethanol/benzylamine (FEB) solutions in an Ar atmosphere at 950°C. Using Raman spectroscopy, we noted that as the N content is increased in the starting FEB solution, the growth of large diameter tubes is inhibited. We observed that the relative electrical conductivity of the strands increases with increasing nitrogen concentration. Thermogravimetric analysis (TGA) showed novel features for highly doped tubes, that are related to chemical reactions on N sites.

Department dc:contributor.department

Massachusetts Institute of Technology. Dept. of Materials Science and Engineering.

Grantor dc:publisher

Massachusetts Institute of Technology

Year dc:date.issued

2006

Author dc:creator

• Villalpando Paéz, Federico

Advisor dc:contributor.advisor

• Mildred S. Dresselhaus and Francesco Stellacci.

• Materials Science and Engineering.

Statement dc:rights

• M.I.T. theses are protected by copyright. They may be viewed from this source for any purpose, but reproduction or distribution in any format is prohibited without written permission. See provided URL for inquiries about permission.

Licence dc:rights.uri

• http://dspace.mit.edu/handle/1721.1/7582

Language dc:language.iso

eng

Handle dc:identifier.uri

http://hdl.handle.net/1721.1/36215

OAI identifier oai:identifier

oai:dspace.mit.edu:1721.1/36215